HOME Parker Products ParkerStores Parker Catalogs INDUSTRIAL CATALOGS Global Industrial Feedback
Fittings Hose & Tubing Quick Couplers Valves Equipment Abrasives Assortments
Fasteners Electrical Cutting Tools Chemicals Fleet & Automotive Universal Parts MSDS  Sheets
Abrasives
Adhesives
Air Preparation

Anchors

Assortments
Automotive

Belts, Industrial
Bolts
Brass Fittings
Camozzi
Cap Screws
Chain 
Chemicals
Clamps
Cutting Tools
Drill Bits
Electrical
Fittings
Fuses

Hydraulic Fittings

Hydraulic Hose
Industrial Hose
Key Stock

Keys
Machine Screws
Metric Fasteners
Nuts
"O" Rings

Paint
Rings & Pins
Rivets

Set Screws
Sheet Metal Screws
Socket Products

Springs

Stainless Fasteners

Tape
Taps
Terminals
Threaded Rod
Tubing
Valves
Washers
Welding
Wheels
Wire
WireTies


#104  & #114

High strength, easy flow, cadmium-free, flux coated silver braze alloy.
Excellent wetting action on a wide range of metals.
Color is silver to light yellow, similar to brass.
Designed for the food and drug industries.
For uses such as: copper, nickel alloys, brass, stainless steel & carbon steel, bronzecarbides
Technical Data (Typical Values)
Tensile Strength up to 73,000 psi (500 N/mm2) //////
Working Temperature 690C (1275F)
Elongation 24%
Corrosion Resistance Good
Diameter (mm) 1.6.........2.5
Classifications Similar to:
AWS/SFA 5.8/ B-Ag 5///////////////////////.//////
DIN 8513 L-Ag 44
For best results, use a slightly carburizing flame.
Bare rod also available as # 114.

#130

Super strength, general use brazing rod.
Excellent for overlaying & build-up at low temperatures (760-870C).
Excellent for close fitting joints, thin-flowing at high temperatures (900-955C).
Designed to build-up or join carbon steels, alloy steels, cast iron, and many 
           non-ferrous materials.
Super active flux promotes ultra-thin flowing of alloy.
For uses such as:
         gear teeth build-up, attaching carbide cutting tips, build-up of bearing shafts,
         joining bicycle assemblies, brazing of rusty surface, heavy equipment repair
...Technical Data (Typical Values)
Tensile Strength up to up to 70,000 psi (483 N/mm2) ....
Working Temperature 760-955C (1400-1750F)
Remelt Temperature 980C (1800F )
Hardness HB 135
Chemistry Cu........Ni....... Zn
  48........10.... ...42
Diameter (mm) 1.6...... 2.5.......3.2
Classifications Similar to:
AWS/SFA 5.8/ RB CuZn-D///////.//////
DIN 8513 L-CuNi10Zn 42
................
For best results, use a neutral flame.

X42

 